化学成分Chemical composition (wt %) :
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
0.02Max
|
0.15Max
|
0.15Max
|
0.010Max
|
0.015Max
|
19.0~21.0
|
Ni
|
Ti
|
Fe
|
Mo
|
B
|
Co
|
33.0~37.0
|
1.0 Max
|
1.0 Max
|
9.0~10.5
|
0.010Max
|
Balance
|
力学性能 Mechanical property :
standards
|
AMS 5844/5845
|
AMS 5758
|
企标
|
Condition
|
Aging
|
HeatTreated
|
Aging
|
Aging
|
Rm (MPa)
|
≥1793
|
793~1000
|
≥1793
|
≥1800
|
Rp0.2 (MPa)
|
≥1586
|
241~448
|
≥1586
|
≥1590
|
A (%)
|
≥8
|
≥50
|
≥8
|
≥8
|
Z (%)
|
≥35
|
≥65
|
≥35
|
≥35
|
Hardness , HRC
|
≥38
|
≤241 HB
|
/
|
38~52
|
物理性能Physical property :
熔点(近似),℃
|
1440
|
密度 d, g/cm3
|
8.43
|
弹性模量 E,MPa(25℃)
|
234500
|
弹性模量 E,MPa(230℃)
|
219000
|
剪切模量 G,MPa(25℃)
|
80950
|
平均线膨胀系数 αm 20~200℃ ,10-6/℃
|
13
|
电阻率 ρ, Ω.m
|
103×10-8
|
热导率,W/m·K(25℃)
|
11.2
|
相对磁导率
|
1.0009
|
抗腐蚀性能 Corrosion resistance :
满足NACE MR0175标准的相关要求
Be able to meet the standard NACE MR0175
可供规格Product forms & sizes (mm):
丝&棒Wire & Bar φ0.5~φ12
参照标准:Reference standards
AMS 5844/5845 AMS 5758
|
NACE MR 01-75
|
ANSI/ASTM F562
|
企标
|